By keeping passenger comfortably seated, minimize in car noise, our auto interior decoration systems work behind the scenes to make driving more enjoyable.

ADVANTAGE

Polyurethane flexible foam is mainly used in car seat cushion, back and headrest. High resilience cold moulding seat can be produced in a combination with two or more hardness, by using two kinds of formula through a single head, double head or multi head mixed into the mould. The cushion is soft in the middle provides comfort, and supportive on two edges provide stability when the vehicle fastly turning around, maintain balance, and keep the body stable, improve the driving comfort and safety.

PROCESS

High resilience cold moulding seat can be produced in a combination with two or more hardness, by using two kinds of formula through a single head, double head or multi head mixed into the mould. PIP process (Pour-in-Place-Technology) is used to produce the pillow, and the polyurethane raw material is directly poured into the pillow cover for inside foaming. The PIP process improves the appearance of the headrest, makes it more in line with ergonomic design, better coordination with the seat, improves the overall visual effect, and reduces energy consumption.

TECHNOLOGY

Rich technical experience, customized according to customer requirements

Application

GB Standard
QC/T 850-2011 Polyurethane foam for seating of passenger car
Typical Performance

Typical Performance

 Grade 

Indentation force deflection(%)

Height loss(%)

Application area (recommended)

A

≤15

≤4

Front seat cushion, sports car seat cushion

B

≤20

≤4

Front seat cushion

C

≤25

≤6

Front seat backrest, rear seat cushion

D

≤30

≤6

Back seat backrest

 

Physical property

Property requirement

Grade A

Grade B

Grade C

Grade D

Core density(kg/m³)

≥48

≥40

≥32

≥24

Indentation Force Deflection (IFD)(%)65%/25%

≥2.7

≥2.6

≥2.5

≥2.4

Elastic resilience(%)

≤20

≤23

≤26

≤30

Tensile strength(kPa)

≥90

≥90

≥82

≥82

Dry aging (Tensile strength)(%)

≤25

≤25

≤25

≤25

Elongation at break(%)

≥120

≥120

≥100

≥100

Tear strength(N/m)

≥240

≥220

≥200

≥180

Compression set(50%)(%)

≤7

≤8

≤9

≤12

Compression set(75%)(%)

≤9

≤11

≤12

≤15

Wet compression set(50%)(%)

≤12

≤13

≤15

≤15

Wet compressive strength set(%)

≤25

≤25

≤30

≤30

Resilience (ball rebound)(%)

≥60

≥55

≥55

≥55

*QC/T 850-2011 Polyurethane foam for seating of passenger car